LRA52
LRA52 Clear thixotropic polyester (PE) primer / sanding sealer
Clear thixotropic polyester primer: holds on vertical faces without sagging and sands easily. Cured with LOB810 peroxide hardener plus LOB828/LOB6AA1 accelerator (2 % each), thinned with S10/S11 (10 %). Spray at 150–200 g/m².
- build/pore-filling sealer under gloss and closed-pore finishes
- priming vertical surfaces, edges and doors where a standard PE primer would sag
- levelling coat under PU/PE lacquers and enamels (after sanding — it does not self-level well on flat panels)
Mix calculator
Ask about LRA52
Answers are based on the LRA52 data and the products it mixes with.
Mixing matrix
- LOB828 / LOB6AA1Accelerator% by weight: 2 %official% by volume: 2 %official
Standard recipe (20 °C). Either accelerator, not both.
Stir the accelerator into the base first, then add LOB810. NEVER pour accelerator and hardener straight into each other — violent reaction, fire risk. Technocolor does not say how LOB828 and LOB6AA1 differ.
- LOB810Hardener% by weight: 2 %official% by volume: 2 %official
Standard hardener for polyester materials.
Dealer: 'hardener for polyester materials', made by MILESI.
- S10Thinner% by weight: 10 %official% by volume: 10 %official
Main thinner for PE primers: fast, strong solvency. Normal shop conditions, thin to medium coats.
S10: s.g. 0.790 ± 0.01, fast, also usable for gun cleaning (official). 2025-26 catalog: S10 is the PE-primer thinner.
- S11Thinner% by weight: 10 %official% by volume: 10 %official
Medium evaporation — for hot shops (above ~25 °C) and large panels so the film flows before it skins.
S11: s.g. 0.81 ± 0.01 (official); catalog lists it as medium-evaporation thinner for PE gloss lacquers.
- % by weight: 10–15 %recommended% by volume: 10–15 %recommended
If the mix spits or you are on a small tip — 15 % max.
More thinner = less build and less sag resistance.
- LOB5Hardener% by weight: 2 %recommended% by volume: 2 %recommended
Longer pot life needed: heat, big batches, airmix/airless; or heavy film builds.
Dealer LOB5: slow drying, even through-cure, extends pot life. Not an official LRA52 recipe — test panel first.
| Role | Material | % by weight | % by volume | When |
|---|---|---|---|---|
| Accelerator | LOB828 / LOB6AA1 | 2 %official | 2 %official | Standard recipe (20 °C). Either accelerator, not both.Stir the accelerator into the base first, then add LOB810. NEVER pour accelerator and hardener straight into each other — violent reaction, fire risk. Technocolor does not say how LOB828 and LOB6AA1 differ. |
| Hardener | LOB810 | 2 %official | 2 %official | Standard hardener for polyester materials.Dealer: 'hardener for polyester materials', made by MILESI. |
| Thinner | S10 | 10 %official | 10 %official | Main thinner for PE primers: fast, strong solvency. Normal shop conditions, thin to medium coats.S10: s.g. 0.790 ± 0.01, fast, also usable for gun cleaning (official). 2025-26 catalog: S10 is the PE-primer thinner. |
| Thinner | S11 | 10 %official | 10 %official | Medium evaporation — for hot shops (above ~25 °C) and large panels so the film flows before it skins.S11: s.g. 0.81 ± 0.01 (official); catalog lists it as medium-evaporation thinner for PE gloss lacquers. |
| Thinner | S10 / S11 | 10–15 %recommended | 10–15 %recommended | If the mix spits or you are on a small tip — 15 % max.More thinner = less build and less sag resistance. |
| Hardener | LOB5 | 2 %recommended | 2 %recommended | Longer pot life needed: heat, big batches, airmix/airless; or heavy film builds.Dealer LOB5: slow drying, even through-cure, extends pot life. Not an official LRA52 recipe — test panel first. |
Percentages are per 100 parts of component A.
Characteristics
- Solids
- 90–98 % part Arecommended
- Viscosity
- high — thixotropic gel at rest; not measurable on a 4 mm cuprecommended
- Density
- not published (expect ≈1.1–1.2 g/cm³)recommended
- Gloss
- n/a (primer)recommended
- Pot life
- 0.25–0.5 hrecommended
- Drying · Dust-free
- 20–40 minrecommended
- Drying · Touch-dry
- 40–60 minrecommended
- Drying · Before sanding
- 8–12 hrecommended
- Drying · Fully dry
- 24–48 hrecommended
- Drying · Conditions
- 20 °C, 2 % LOB810 + 2 % accelerator (assumed reference conditions)
- Hardness
- high (PE family)recommended
- Elasticity
- low — hard and brittle in thick buildsrecommended
- Chemical resistance
- high physical-chemical resistance (PE family statement)catalog
- Shrinkage
- practically no shrink-back over time (PE family statement)catalog
- Lightfastness
- PE can shift the colour of an underlying staincatalog
- Thixotropy
- yesofficial
- Sandability
- good — sands easilyofficial
- Cure mechanism
- radical cure of unsaturated polyester/styrene: peroxide hardener (LOB810) + metal-salt accelerator (LOB828/LOB6AA1)recommended
Application
Conventional spray
- Nozzle
- 1.8–2.2 (typ. 2) mmrecommended
- Pressure · air
- 3–4 barrecommended
- Spray viscosity
- 35–60 s DIN4 (indicative)recommended
- Consumption
- 150–200 g/m²official
- Wet film
- 130–180 µmrecommended
- Coats
- 1–2 coatsrecommended
- Flash-off
- 30–40 minrecommended
- Recoat
- second LRA52 coat after 30–40 min (gelled, still tacky-firm); topcoat only after sanding at ~12 hrecommended
- Sanding between coats
- none between PE coats laid wet-on-gel; after ~12 h sand P240→P320 under pigmented/PU topcoats, P360–P400 under clear glossrecommended
Stir well before filling the cup — the thixotropic primer stiffens at rest. Mix only 15–20 min worth; flush the gun with S10 straight after — cured PE won't wash out.
HVLP
- Nozzle
- 1.8–2.5 (typ. 2) mmrecommended
- Pressure · air
- 2–2.5 bar at inlet (trigger pulled), ≤0.7 bar at caprecommended
- Spray viscosity
- 35–60 s DIN4 (indicative)recommended
- Consumption
- 150–200 g/m²official
- Coats
- 1–2 coatsrecommended
15–20 cm distance, 50 % overlap. Heavy orange peel — don't thin past 15 %, fit a bigger tip instead.
Airless
- Nozzle
- 0.28–0.33 mm (tip 011–013 thou)recommended
- Pressure · fluid
- 120–180 barrecommended
- Consumption
- 150–200 g/m²official
Short PE pot life in a pump/hose is risky: small batches or slow LOB5 hardener (test first), flush with S10 on any break.
Airmix (air-assisted airless)
- Nozzle
- 0.28–0.33 mm (≈011–013 thou airmix tip)recommended
- Pressure · fluid
- 12–20 barrecommended
- Pressure · air
- 1–2 barofficial
- Consumption
- 150–200 g/m²official
Same pot-life cautions as airless.
Process and compatibility
- Substrate preparation
- bare wood/veneer/MDF sanded P150–P180 (P220 on MDF), dust removed; wood moisture 8–12 %recommended
- Sanding
- after ~12 h at 20 °C: P240→P280→P320 under pigmented/PU gloss, P360–P400 under clear glossrecommended
- Temperature and humidity
- 18–25 °C material and room, RH ≤ 75 %; not below 15 °Crecommended
- Don'ts
- never pour LOB828/LOB6AA1 accelerator and LOB810 hardener into each other — add each to the base in turn
- don't mix more than you can spray in 15–20 min
- don't leave mixed material in the gun/hose — flush with S10 at once
- don't thin past 15 % — you lose thixotropy and build
- don't spray over oily/resinous species without an isolating primer
- don't go over a stain without a test panel — PE can shift the stain colour
- don't sand before ~12 h at 20 °C — paper clogs
- don't expect it to flow out on flat horizontal panels — thixotropic primer levels worse (orange peel, unfilled pores)
Storage
- Shelf life
- not published (typically 6–12 months)recommended
- Storage temperature
- 5–25 °Crecommended
- Packaging
- not publishedrecommended
Safety: Contains styrene — toxic and flammable. Spray in an extracted booth wearing an A2 organic-vapour respirator, gloves and goggles. LOB810 peroxide hardener is an oxidiser: store apart from the accelerator, never let them touch each other, rags or metal swarf. Eye splash — rinse and see a doctor. Soak rags with mixed material in water.
Sources
Value tags: “official”, “dealer”, “catalog”, “schedule” are Technocolor data; “workshop” is from our own datasheets; “recommended” comes from industry best practices (hover to see the reasoning).
- official: thixotropic, sands well; spray 150–200 g/m²; LOB810 2 %/2 %; S10/S11 10 %/10 %; LOB828/LOB6AA1 2 %/2 %
- dealer search: LRA52 not stocked/listed (no product page)
- dealer: LOB810 hardener for polyester materials, MILESI
- dealer: LOB5 slow PE hardener, MILESI — cold conditions, thick films, longer pot life
- official: S10 s.g. 0.790 ± 0.01, fast, for cleaning too
- official: S11 thinner for PE, s.g. 0.81 ± 0.01
- official sibling LRA98 (non-thixotropic) mix table
- official sibling LRA923 (high clarity, more elastic) mix table
- 2019 catalog: PE drawbacks (toxicity, limited pot life, stain colour shift); peroxide hardener + cobalt-salt catalyst; sibling solids ETS20 ~92 %, EPS20 ~98 %, EPS22 98.5 %
- official application methods: airless ≤200 bar for primers on flat panels, airmix ≤20 bar + 1–2 bar air
- official characteristics vocabulary (thixotropy, pot life, drying stages, hardness/brittleness)
- official schedule (ETS50 PE primer on oak) — analogue for recoat/sanding
Not covered by the sources
- No dealer product page on t-colormarket.ru (search for LRA52 returns nothing) — solids, viscosity, pot life, drying times all unpublished
- No Milesi/Technocolor TDS or SDS found for LRA52, LOB810, LOB828, LOB6AA1 (faichim.com and edid-milesi.bg guesses 404; not found by search)
- Difference between accelerators LOB828 and LOB6AA1 not published
- Density of part A not published (official volume % = weight % for thinner is not physically consistent, so cannot back-calculate)
- Pot life, dust-free/touch/sand/full-cure times — only derived from sibling PE primers
- Hardness, elasticity, lightfastness values (pencil/König/Erichsen) not published
- Shelf life, packaging not published
- LRA52 not used in any official finishing schedule; schedule data cited only as analogues from ETS50/EPS20
- LOB5 (slow Milesi PE hardener) compatibility with LRA52 is an inference, not official
- Ask Technocolor for the Milesi TDS of LRA52 (likely Milesi 'fondo poliestere tixotropico')
- Spray viscosity (DIN4) is an estimate; no flow-cup figure exists for LRA52 and thixotropic materials read unreliably in a cup